Welding Position
|
|||||||||||||
All Positions
|
|||||||||||||
Welding Instruction
|
|||||||||||||
(1) Clean up the contaminations on the steel.
(2) Dry the electrodes at 350~400°C for 60 minutes before welding.
(3) Keep arc as short as possible. Take the back step method to prevent porosity at arc start and re-start. (Please refer to Appendix A).
(4) Preheat and interpass temperature:100~200°C, PWHT:600~635°C.
|
|||||||||||||
TypicalChemical Composition of Weld Metal (wt %)
|
|||||||||||||
C
|
Si
|
Mn
|
P
|
S
|
Mo
|
||||||||
0.080
|
0.54
|
0.78
|
0.012
|
0.011
|
0.56
|
||||||||
TypicalMechanical Properties of Weld Metal(PWHT:620°Cx1Hr)
|
|||||||||||||
Tensile Strength
N/mm2(kgf/mm2)
|
Yield Strength
N/mm2(kgf/mm2)
|
Elongation
%
|
Charpy V-Notch
|
||||||||||
°C
|
J (kgf -m)
|
||||||||||||
570(58.1)
|
490(50.0)
|
31
|
0
|
—
|
|||||||||
-29
|
—
|
||||||||||||
Size and SuggestedOperating Range (AC or DC+)
|
|||||||||||||
Diameter (mm) x Length(mm)
|
3.2x350
|
4.0x400
|
5.0x400
|
|
|||||||||
Amp
|
F
|
90~140
|
140~190
|
180~240
|
|
||||||||
V-up/OH
|
80~120
|
120~160
|
—
|
|