| Product name：KL-916B3 |
| Classification：A5.5 / E9016-B3 |
  |
- KL-916B3 is suitable for welding Cr-Mo alloy steel.
- Weld metal contains 2.25%Cr-1%Mo.
- It provides great creep resistance at 550°C.
- It is ideal for welding high pressure steel pipes and heat exchanger steel pipes, such as ASTM A387Gr.22 and JIS SCMV4.
|
Welding Position
|
|
|||||||||||||
|
All Positions
|
|
|||||||||||||
|
Welding Instruction
|
|
|||||||||||||
|
(1) Clean up the contaminations on the steel.
(2) Dry the electrodes at 350~400°C for 60 minutes before welding.
(3) Keep arc as short as possible. Take the back step method to prevent porosity at arc start and re-start. (Please refer to Appendix A)
(4) Preheat and interpass temperature: 160~190°C, PWHT: 675~705°C.
|
|
|||||||||||||
|
TypicalChemical Composition of Weld Metal (wt %)
|
|
|||||||||||||
|
C
|
Si
|
Mn
|
P
|
S
|
Cr
|
Mo
|
|
|||||||
|
0.070
|
0.68
|
0.87
|
0.015
|
0.009
|
2.14
|
0.95
|
|
|||||||
|
TypicalMechanical Properties of Weld Metal(PWHT:690°Cx1Hr)
|
|
|||||||||||||
|
Tensile Strength
N/mm2(kgf/mm2)
|
Yield Strength
N/mm2(kgf/mm2)
|
Elongation
%
|
Charpy V-Notch
|
|
||||||||||
|
°C
|
J (kgf -m)
|
|
||||||||||||
|
670(68.3)
|
590(60.2)
|
24
|
0
|
—
|
|
|||||||||
|
-29
|
—
|
|
||||||||||||
|
Size and SuggestedOperating Range (AC or DC+)
|
||||||||||||||
|
Diameter (mm) x Length(mm)
|
3.2x350
|
4.0x400
|
5.0x400
|
|||||||||||
|
Amp
|
F
|
90~140
|
140~190
|
180~240
|
||||||||||
|
V-up/OH
|
80~120
|
120~160
|
—
|
|||||||||||