Product name：KS-317L
 
Classification：A5.4 / E317L-16
 
 

  1. Weld metal is 19%Cr-12%Ni-3%Mo, which is suitable for welding AISI 317L steel.
  2. It provides good corrosion and heat resistance due to its low C and additional Mo content.
  3. It has good strength at high temperature and post weld heat treatment is not required.
  4. It is ideal for welding critical chemical vessels for sulfuric and sulphurous acid.

 

Welding Position

All Positions

Typical Chemical Composition of Weld Metal (wt. %)

C

Si

Mn

P

S

Cr

Ni

Mo

0.034

0.36

1.49

0.015

0.010

19.61

13.85

3.52

Typical Mechanical Properties of Weld Metal

Tensile Strength

N/mm2（kgf/mm2）

Yield Strength

N/mm2（kgf/mm2）

Elongation

%

5% Sulfuric Acid Corrosion Test (g/m2hr)

580(59.1)

430(43.8)

41

≦5

Size and Suggested Operating Range (AC or DC+)

Diameter x Length (mm)

2.0x250

2.6x300

3.2x350

4.0x350

5.0x350

Amp

F/H-Fillet

35~55

50~85

80~120

100~150

140~200

V-up/OH

30~50

45~85

70~110

90~135

—