Welding Instruction

1. Clean the surface of the base metal before welding.
2. It is difficult for welding in V & O-H positions, so F welding is recommended.
3. Baking temperature should be between 350~400°C during 30~60 minutes before welding. No PWHT is required for base metal.
4. To avoid weave arc, make a short arc in low current.

Typical Chemical Composition of Weld Metal (wt %)

C

Si

Mn

P

S

Ni

Ti

Fe

Cu

0.040

0.68

3.18

0.009

0.008

66.50

0.18

0.51

Rem.

Typical Mechanical Properties of Weld Metal

Tensile Strength

N/mm²（kgf/mm²）

Yield Strength

N/mm²（kgf/mm²）

Elongation

%

Charpy V-Notch

°C

J（Kgf-m）

500(51.0)

310(31.6)

43

-196

100(10.2)

Size and Suggested Operating Range (DC+)

Diameter (mm) x Length(mm)

2.6x300

3.2x350

4.0x350

4.8x350

Amp

H

60~85

70~115

95~145

140~180

V/O-H

55~85

65~110

85~135

—